Batch | Angle of repose (°) | Bulk density (g/cm3) | Tapped density (g/cm3) | Compressibility Carr’s index | Hausner’s ratio |
---|---|---|---|---|---|
TSP1 | 28.61 ± 0.12 | 0.492 ± 0.02 | 0.579 ± 0.02 | 15.25 ± 0.01 | 1.18 ± 0.09 |
TSP2 | 28.24 ± 0.11 | 0.495 ± 0.01 | 0.582 ± 0.01 | 15.21 ± 0.03 | 1.19 ± 0.07 |
TSP3 | 28.76 ± 0.09 | 0.488 ± 0.02 | 0.575 ± 0.02 | 15.18 ± 0.05 | 1.17 ± 0.04 |
TSP4 | 28.85 ± 0.08 | 0.491 ± 0.02 | 0.581 ± 0.02 | 15.28 ± 0.1 | 1.16 ± 0.04 |
TSP5 | 28.58 ± 0.13 | 0.493 ± 0.01 | 0.576 ± 0.01 | 15.23 ± 0.02 | 1.18 ± 0.03 |
TSP6 | 28.45 ± 0.14 | 0.489 ± 0.03 | 0.585 ± 0.02 | 15.18 ± 0.09 | 1.19 ± 0.05 |
TSP7 | 28.39 ± 0.11 | 0.491 ± 0.02 | 0.574 ± 0.02 | 15.21 ± 0.03 | 1.17 ± 0.06 |
TSP8 | 28.67 ± 0.15 | 0.486 ± 0.01 | 0.579 ± 0.01 | 15.26 ± 0.04 | 1.18 ± 0.01 |
TSP9 | 28.51 ± 0.12 | 0.494 ± 0.02 | 0.580 ± 0.02 | 15.22 ± 0.02 | 1.19 ± 0.04 |
TSP10 | 28.73 ± 0.11 | 0.491 ± 0.01 | 0.578 ± 0.02 | 15.28 ± 0.03 | 1.18 ± 0.10 |
TSP11 | 28.43 ± 0.15 | 0.486 ± 0.01 | 0.586 ± 0.02 | 15.21 ± 0.1 | 1.17 ± 0.09 |
TSP12 | 28.58 ± 0.15 | 0.488 ± 0.02 | 0.575 ± 0.01 | 15.26 ± 0.04 | 1.16 ± 0.03 |
TSP13 | 28.34 ± 0.09 | 0.490 ± 0.02 | 0.571 ± 0.01 | 15.22 ± 0.05 | 1.18 ± 0.05 |
TSP14 | 28.57 ± 0.11 | 0.493 ± 0.02 | 0.576 ± 0.01 | 15.18 ± 0.07 | 1.18 ± 0.09 |
TSP15 | 28.69 ± 0.10 | 0.499 ± 0.03 | 0.578 ± 0.01 | 15.21 ± 0.1 | 1.2 ± 0.10 |
TSP16 | 28.24 ± 0.07 | 0.487 ± 0.02 | 0.584 ± 0.02 | 15.23 ± 0.06 | 1.18 ± 0.11 |
TSP17 | 28.56 ± 0.17 | 0.491 ± 0.02 | 0.572 ± 0.02 | 15.16 ± 0.08 | 1.19 ± 0.03 |
TSP18 | 28.49 ± 0.14 | 0.493 ± 0.01 | 0.577 ± 0.01 | 15.22 ± 0.01 | 1.17 ± 0.04 |
TSP19 | 28.53 ± 0.12 | 0.490 ± 0.02 | 0.579 ± 0.01 | 15.25 ± 0.06 | 1.20 ± 0.03 |
TSP20 | 28.58 ± 0.11 | 0.489 ± 0.02 | 0.578 ± 0.02 | 15.18 ± 0.09 | 1.18 ± 0.04 |